Buy low iron ultra clear float Solar Glass For BIPV Module China Brands
- DONGKE
- HANGZHOU,CHINA
- 7-15DAYS
- 2400.0000SQM/YEAR
1). Smooth and flat surface and good vision
2). Excellent optical performance
3). Stable chemical properties
4) Resistant to acid, alkaline and corrosion.
5). Flexible size specifications, minimizing cutting loss
6). Substrata for each level of glass processing
7) . Applications: architecture, furniture, mirrors
China black printed backside float white/black printed back Glass 2mm 2.5mm 3.0mm with holes For BIPV panel Module
2.0mm 2.5mm 3.0mm black white printed backside float glass is also called flat glass which mainly used on back of BIPV panel which also called Double glasses panel, BIPV panel is a thin layer of optoelectronic semiconductor which converting solar energy into electricity. By considering its efficiency, we are using High- transmittance and low reflection glass for its panel. This high strength glass maintains the best image quality by eliminating unwanted distortions with the advanced optical technology.
Feature:
1.Thickness: 2.0mm~10mm;
2.Standard thickness: 2.0mm.3.2mm and 4.0mm 5.0mm
3.Thickness Tolerance: 3.2mm± 0.20mm; 4.0mm± 0.30mm
4.Max size: 2250mm× 3300mm
5.Min size: 300mm× 300mm
6.Solar Transmittance (3.2mm): ≥ 91.6%
7.Iron Content: ≤ 120ppm Fe2O3
8.Poisson's Ratio: 0.2
9.Density: 2.5 g/CC
10.Young's Modulus: 73 GPa
11.Tensile Strength: 42 MPa
12.Hemispherical Emissivity: 0.84
13.Expansion Coefficient: 9.03x10-6/° C
14.Softening Point: 720 ° C
15.Annealing Point: 550 ° C
16.Strain Point: 500 ° C
Terms | condition |
Thickness range | 2.0mm to 16mm(Standard thickness range:3.2mm and 4.0mm) |
Thickness Tolerance | 2.0mm 3.0mm±0.20mm |
Solar Transmittance (3.2mm) | more than 85% |
Iron Content | less than 120ppm Fe2O3 |
Density | 2.5 g/cc |
| Youngs Modulus | 73 GPa |
| Tensile Strength | 42 MPa |
| Expansion Coefficient | 9.03x10-6/ |
Annealing Point | 550 centigrade degrees |